ASTM D Standard Practice for Heat Aging of Plastics Without Load 1 1 x00a0 This practice is intended to define the exposure conditions for evaluating. Standard Practice for Heat Aging of Plastics Without Load – ASTM D Status: Withdrawn ยท Replaced by: ASTM D Buy this standard. Price: . ASTM D(). Standard Practice for Heat Aging of Plastics Without Load. standard by ASTM International, 03/15/ This document has been.

Author: Dura Arasho
Country: Poland
Language: English (Spanish)
Genre: Sex
Published (Last): 25 December 2018
Pages: 315
PDF File Size: 5.26 Mb
ePub File Size: 17.61 Mb
ISBN: 677-8-43007-346-9
Downloads: 21547
Price: Free* [*Free Regsitration Required]
Uploader: Moogujar

Certain materials are susceptible to the influence of humidity. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Normally, additional shrinkage should be expected with loss of volatiles or advance in polymerization. A plastic material is not necessarily degraded by exposure to elevated temperatures.

The effect of elevated temperature on any particular property is determined by selection of the appropriate test method and test specimens for that property. Caution should be exercised in using the Arrhenius relation and knowledge of physical changes in the material at elevated temperatures is important.

Standard – Standard Practice for Heat Aging of Plastics Without Load ASTM D –

Factors that affect the reproducibility of data are the degree of temperature control of the enclosure, humidity of the oven, air velocity over the specimen, and period of exposure.

With semi-crystalline and highly crystalline polymers, elevated temperatures may cause significant changes d304 the morphology of the material, invalidating or compromising that assumption. Add to Alert PDF.

The severity of the exposures in both time qstm temperature determines the extent and type of change that takes place. Already Subscribed to this document.

This standard is not included in any packages. Recommended procedures for determining the thermal aging characteristics of a material using a series of elevated temperatures for the purpose of estimating endurance time to a defined property change at a lower temperature are also described; the applicability of the Arrhenius relation for making predictions to other temperatures, is assumed in this case.

  MAHARASHTRA KILLE PDF

Different atsm, mechanical or electrical, may not change at the same rate. Need more than one copy? Errors in exposure are cumulative with time. The property of interest is measured at room temperature.

Your Alert Profile lists the documents that will be monitored. If the document is revised or amended, you will be notified by email. For instance, the arc resistance of thermosetting compounds improves up to the carbonization point of the material. You can download and open this file to your own computer but DRM prevents opening atsm file on another computer, including a networked server. Please first log in with a verified email before subscribing to alerts.

Arrhenius principles may only be used to accelerate a chemical mechanism if there are no fundamental changes in the material properties. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. Specific properties and failure or lifetime criteria for these properties are typically chosen for the evaluation of thermal endurance. However, extended periods of exposure of plastics to elevated temperatures will generally cause some degradation, with progressive changes in physical properties.

Ultimate properties such as strength or elongation are more sensitive to degradation than bulk properties such as modulus, in most cases. Only the procedure for heat exposure is specified. These transitions should be avoided both in the range of aging temperatures used, as well as in extrapolation of the lifeline. Standards Subscriptions from ANSI provides a money-saving, multi-user solution for accessing standards. On the contrary, this practice is designed to provide data which can be used for such comparative purposes.

Standards Subsctiption may be the perfect solution. Work Item s – proposed revisions of this standard. However, the data obtained from this practice, since it does not account for the influence of stress or environment that is involved in most real life applications, must be used cautiously by the designer, who must inevitably make material choices using additional data such as creep and creep rupture that are consistent with the requirements of the specific application.

  AGUA ENVENENADA FERNANDO BENITEZ PDF

We have no amendments or corrections for this standard. Therefore, for any application of the CUT or the TI temperature index to be valid, either the thermal aging program must duplicate the intended thermal exposure conditions of the end product, or the Arrhenius relation must apply.

This standard and ISO address the same subject matter but differ in technical content. This standard and ISO address the same subject matter but differ in technical content. This standard is also available to be included in Standards Subscriptions. As the voice of the U. Please first verify your email before subscribing to alerts.

Historical Version s – view previous versions of standard. It is the responsibility of the user of this standard asmt establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

Standard Practice for Heat Aging of Plastics Without Load

The property of interest is measured at room temperature. Link to Active This link will always route to the current Active version of the standard. The effect of elevated dd3045 on any particular property is determined by selection of the appropriate test method and test specimens for that property.

Mechanical properties, such as flexural properties, are sensitive to heat degradation and may change at a more rapid rate.

Recommended procedures for determining the thermal aging characteristics of a material using a series of elevated temperatures for the purpose of estimating endurance time axtm a defined property change at a lower temperature are also described; the applicability of the Arrhenius relation for making predictions to other temperatures, is assumed in this case.

Proceed to Checkout Continue Shopping. Only the procedure for heat exposure is specified.