Originally approved in Last previous edition approved in as B – 2 For referenced ASTM standards, visit the ASTM website. ASTM B(). Standard Specification for Titanium and Titanium Alloy Castings. standard by ASTM International, 11/01/ View all product details. ASTM B Standard Specification for Titanium and Titanium Alloy Castings.

Author: Mukinos Kejora
Country: Mexico
Language: English (Spanish)
Genre: Marketing
Published (Last): 16 February 2016
Pages: 302
PDF File Size: 11.13 Mb
ePub File Size: 17.73 Mb
ISBN: 610-3-23677-969-5
Downloads: 48058
Price: Free* [*Free Regsitration Required]
Uploader: Malak

ASTM B – 13() Standard Specification for Titanium and Titanium Alloy Castings

The procedures developed shall be consistent with standard practices recommended for reactive metal alloys. The chemical composition determined shall conform to the requirements speci?

Other surface discontinuities shall meet the visual acceptance standards speci? This is in accordance with the round-off method of Practice E A superscript epsilon e indicates an editorial change since the last revision or reapproval. By agreement between producer and purchaser, analysis may be required and limits established for elements or compounds not speci?

If a casting is used for a hardness sample, indentations shall be made in a surface that will not be subsequently machined.

Materials and Manufacture 5. The producer shall not ship material which is outside the limits speci? Workmanship, Finish, and Appearance 8. The results shall conform to the requirements speci? Hardness shall be determined in the as-cast condition unless otherwise speci? Last previous edition B — Need not be reported. Small size castings may be such that marking must be limited consistent with the available area.

When discontinuities exceed the acceptance limits, all castings in the lot shall be examined according to Category II. A number in parentheses indicates the year of last reapproval. The stressrelief cycle shall be in accordance with 7.

ASTM B – 09 Standard Specification for Titanium and Titanium Alloy Castings

If the pattern is supplied by the purchaser, the dimensions of the casting shall be as predicted by the pattern. This specification covers the standard requirements for titanium and titanium alloy castings intended for general corrosion resistant and industrial applications.

  EARMYU STATEMENT OF UNDERSTANDING PDF

Inspection procedure shall be in accordance with the Guide E 94 and Method E All castings shall be supplied in the as-cast condition except when post-weld heat treatment is required wherein it shall consist of a stress relief performed at certain temperatures. This abstract is a brief summary of the referenced standard.

Grade 18—Palladium added to titanium alloy 3AI Unalloyed titanium plus 0. Historical Version s – 3b67 previous versions of standard. If the results for the retest fail to conform to the speci?

The producer shall maintain documentation on procedure and welder quali? Examination of Weld Preparation S3. The surface of the castings shall be free of adhering mold material, scale, cracks, and hot tears as determined by visual inspection.

Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. Link to Active This link will always route to the current Active version of the standard.

Time at temperature shall be a minimum of 1? Liquid Penetrant Examination S2. Areas to be inspected, ast and types of liquid penetrants to be used, developing procedure, and basis for acceptance shall be agreed upon between the producer and the purchaser.

It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application.

ASTM B367 GB / T 15073 Titàn Graphite Ponp Distribisyon pou Vann

Tensile Strength, min, 0. Originally published as B — 61 T.

Types and degrees of discontinuities considered shall be judged by the Reference Radiographs E After heat treatment, the castings should be cooled in air or in the furnace to ambient temperature unless otherwise agreed upon between the purchaser and producer. Typical methods include the consumable electrode and induction-slag, plasma arc, induction-skull, and electron beam melting processes. Tensile properties shall be determined using a strain rate of 0.

  DOMINIC SCOTT PLATO MENO PDF

The values given in parentheses are for information only. The test report shall contain the results of the actual chemical analysis and other tests speci? The examination shall be in accordance with Practice E Dimensional tolerances shall be included on the casting drawing, 4.

The American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard. The chemical composition determined shall conform to the analysis in Table 1 within the check analysis variations shown in Table 2 or shall be subject to rejection by the purchaser. Current edition approved Aug. Product analysis limits shall be as speci?

ASTM B367 F67 F136 Ti Pure Titanium Ball Valve

Referenced Documents purchase separately The documents listed below are referenced within the subject standard satm are not provided as part of the standard. Materials for this specification shall be melted by conventional processes used for reactive metals such as consumable electrode and induction-slag, plasma arc, induction-skull, and electron beam melting processes. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

Extent of examination and the basis for b37 shall be agreed upon by the producer and the purchaser. Repair by Welding 9. The stress-relief cycle shall be in accordance with 7. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM Headquarters.